L 1	B or L245	≤0.28	≤1.20	≤0.030	≤0.030	-	-	-	-	-
	x42 or L290	≤0.28	≤1.30	≤0.030	≤0.030	-	-	-	-	-
	X46 or L320	≤0.28	≤1.40	≤0.030	≤0.030	-	-	-	-	-
	X52 or L360	≤0.28	≤1.40	≤0.030	≤0.030	-	-	-	-	-
	X56 or L390	≤0.28	≤1.40	≤0.030	≤0.030	-	-	-	-	-
	X60 or L415	≤0.28	≤1.40	≤0.030	≤0.030	-	-	-	-	-
	X70	≤0.28	≤1.40	≤0.030	≤0.030	-	-	-	-	-
PSL 2	BR or L245R	≤0.24	≤1.20	≤0.025	≤0.015	≤0.40	c	c	≤0.04	≤0.25
	X42R or L290R	≤0.24	≤1.20	≤0.025	≤0.015	≤0.40	≤0.06	≤0.05	≤0.04	≤0.25
	BN or L245N	≤0.24	≤1.20	≤0.025	≤0.015	≤0.40	c	c	≤0.04	≤0.25
	X42N or L290N	≤0.24	≤1.30	≤0.025	≤0.015	≤0.40	≤0.06	≤0.05	≤0.04	≤0.25
	X46N or L320N	≤0.24	≤1.40	≤0.025	≤0.015	≤0.40	≤0.07	≤0.05	≤0.04	≤0.25
	X52N or L360N	≤0.24	≤1.40	≤0.025	≤0.015	≤0.45	≤0.10	≤0.05	≤0.04	≤0.25
	X56N or L390N	≤0.24	≤1.40	≤0.025	≤0.015	≤0.45	≤0.10	≤0.05	≤0.04	≤0.25
	X60N or L415N	≤0.24	≤1.40	≤0.025	≤0.015	≤0.45	≤0.10	≤0.05	≤0.04	-
	X65N or L450N	≤0.24	≤1.40	≤0.025	≤0.015	≤0.45	≤0.10	≤0.05	≤0.04	-
	X70N	≤0.24	≤1.40	≤0.025	≤0.015	≤0.45	≤0.10	≤0.05	≤0.04	-
	X80	≤0.24	≤1.40	≤0.025	≤0.015	≤0.45	≤0.10	≤0.05	≤0.04	-

 ①抗拉强度（σb）试样在拉伸过程中，在拉断时所承受的 力（Fb），除以试样原横截面积（So）所得的应力（σ），称为抗拉强度（σb），单位为N/mm2（MPa）。它表示金属材料在拉力作用下抵抗破坏的 能力。
  ②屈服点（σs）具有屈服现象的金属材料，试样在拉伸过程中力不增加（保持恒定）仍能继续伸长时的应力，称屈服点。若力发生下降时，则应区分上、下屈服点。屈服点的单位为N/mm2（MPa）。上屈服点（σsu）：试样发生屈服而力下降前的 应力；下屈服点（σsl）：当不计初始瞬时效应时，屈服阶段中的小应力。
  屈服点的计算公式为：式中：Fs--试样拉伸过程中屈服力（恒定），N（牛顿）So--试样原始横截面积，mm2。③断后伸长率（σ）在拉伸试验中，试样拉断后其标距所增加的长度与原标距长度的百分比，称为伸长率。
  以σ表示，单位为%。计算公式为：σ=（Lh-Lo）/L0*式中：Lh--试样拉断后的标距长度，mm；L0--试样原始标距长度，mm。④断面收缩率（ψ）在拉伸试验中，试样拉断后其缩径处横截面积的 缩减量与原始横截面积的百分比，称为断面收缩率。
  以ψ表示，单位为%。计算公式如下：式中：S0--试样原始横截面积，mm2；S1--试样拉断后缩径处的少横截面积，mm2。⑤硬度指标金属材料抵抗硬的物体压陷表面的能力，称为硬度。根据试验方法和适用范围不同，硬度又可分为布氏硬度、洛氏硬度、维氏硬度、肖氏硬度、显微硬度和高温硬度等。
  对于管材一般常用的有布氏、洛氏、维氏硬度三种。A、布氏硬度（HB）用一定直径的钢球或硬质合金球，以规定的试验力（F）压入式样表面，经规定保持时间后卸除试验力，测量试样表面的压痕直径（L）。布氏硬度值是以试验力除以压痕球形表面积所得的商。