电工钢硅钢片 DW540-50 0.5*1200免费咨询

电工钢硅钢片近20年来，我国硅钢产业取得了长足的进步，这其中以首钢、西藏那曲当地武钢和宝钢为代表。得益于我国钢铁行业全流程的技术进步，这些企业在控制无取向硅钢整体质量稳定性和取向硅钢方面已经具有较高技术实力。2014年我国硅钢生产达到823万吨，高端产品有20~30万吨的进口量，2015年，我国共生产电工钢约836万吨，进口量进一步下降到14万吨。但是，与日本相比我国在高端电工钢领域仍有不小的差距，这集中体现在高磁感无取向硅钢、西藏那曲当地超低铁损Hi-B取向硅钢和高硅钢等产品上。例如，新日铁公司(现新日铁住金)能够实现0.15~0.35mm系列厚度规格极低铁损Hi-B取向电工钢的稳定供货，引领取向硅钢工艺发展。在特殊用途硅钢方面，日本钢管公司(现JFE)通过气相沉积法(CVD)渗硅的方式实现了高硅钢薄带的供货。随着我国装备制造业的产业升级，高端硅钢产品的需求会越来越迫切。我国与日韩等钢铁强国在这一领域的竞争将会更加激烈，这就要求我国相关科研人员通过革命性创新进行下一代硅钢生产技术的研发，引领世界电工钢技术的发展。低铁损、西藏那曲当地高磁感电机用无取向硅钢、西藏那曲当地薄规格超低铁损高磁感取向硅钢和中高频节能电器用高硅钢是电工钢产业的发展方向。

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Since it is a functional material, its performance testing also revolves around "function". These indicators are often mentioned in trade and processing processes, and a brief understanding can help everyone better carry out their work. The performance testing of electrical steel mainly includes the following aspects: magnetic inspection, stacking coefficient inspection, coating adhesion inspection, repeated bending inspection, size and shape surface inspection, and conventional mechanical property inspection. In addition to the types of products listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, which are used as intermediate and intermediate grade High frequency motors and transformers, as well as pulse transformers, etc； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding. Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength. Magnetic induction strength is the number of magnetic lines passing through a unit cross-sectional area of the iron core, also known as magnetic flux density. It represents the material‘s magnetization ability, measured in T. The magnetic induction strength of electrical steel plates is high, and the excitation current (also known as no-load current) of the iron core is reduced. Copper and iron losses are also reduced, which can save electrical energy. When the power of the motor and transformer remains constant, the magnetic induction intensity is high, and the design Bm can be increased. The cross-sectional area of the iron core can be reduced, which reduces the volume and weight of the iron core, and saves the amount of electrical steel plates, wires, insulation materials, and structural materials used. This can reduce the total loss and manufacturing cost of the motor and transformer, and is beneficial for the manufacturing, installation, and transportation of large transformers and motors. The main requirements for the performance of silicon steel are: 1. Low iron loss is the most important indicator of the quality of silicon steel sheets. Various countries classify grades based on iron loss values, with the lower the iron loss, the higher the grade. 2. Under strong magnetic fields, the magnetic induction intensity (magnetic induction) is high, which reduces the volume and weight of the iron core of the motor and transformer, saving silicon steel sheets, copper wires, and insulation materials. 3. The surface is smooth, flat, and the thickness is uniform, which can improve the filling coefficient of the iron core. 4. Good lamination performance is more important for manufacturing micro and small electric motors. 5. The adhesion and weldability of the surface insulation film are good, which can prevent corrosion and improve the punching performan